Title:

Synthesis of SiO₂ nanoparticles from rice husk ash by precipitation method

Từ khóa:

Hạt nano, kết tủa, nano oxyt silic, tro vỏ trấu, vô định hình

Keywords:

Amorphous, nanoparticles, nanosilica, precipitation, Rice husk ash (RHA)

ABSTRACT

Silica nanoparticles have been successfully prepared from rice husk ash by using precipitation method. At first, the rice husk ash (RHA) was obtained by annealing at temperatures 500 - 700^oC for 4 hours, then nanosilica particles were extracted by using 3N sodium hydroxide solution followed by precipitating with HCl solution to pH = 6. The obtained product was characterized by X-ray diffraction (XRD), Energy-dispersive X-ray spectrometry (EDS), Fourrier Transformation Infrared (FTIR) to determine the crystal lattice structure, phase and elemental composition. The morphology and grain size of the sample were investigated by field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The results showed that the prepared SiO₂ nanoparicles were amorphous phase with the average size about 15 nm.

TóM TắT

Những hạt nano SiO₂ được tổng hợp thành công từ vỏ trấu bằng phương pháp kết tủa. Lúc đầu, vỏ trấu được nung ở nhiệt độ từ 500 - 700^oC trong thời gian 4 h, thu được tro vỏ trấu. Sau đó bột nano Silica được tách chiết từ tro trấu bằng cách sử dụng dung dịch NaOH có nồng độ 3N và tiếp tục thêm dung dịch HCl ở độ pH = 6 cho đến khi dung dịch kết tủa trắng. Sản phẩm bột nano trên được đem đo nhiễu xạ tia X (XRD), tán sắc năng lượng (EDS), quang phổ hồng ngoại biến đổi Fourier để xác định cấu trúc mạng, thành phần pha, nguyên tố và mẫu được đem chụp ảnh hiển vi điện tử quét (FESEM), ảnh hiển vi điện tử truyền qua (TEM)xác định kích thước hạt, hình thái học. Kết quả, những hạt nano SiO₂ chế tạo được có pha vô định hình và kích thước hạt trung bình khoảng 15 nm.