Thông tin chung: Ngày nhận bài: 26/12/2019
Ngày nhận bài sửa: 09/04/2020 Ngày duyệt đăng: 29/06/2020 Title: Synthesizing 3D crystalline metal organic framework based on catecholate linker Từ khóa: Catecholate, cấu trúc tinh thể 3D, srs topology, vật liệu khung cơ kim Keywords: Catecholate, 3D crystalline structures, srs topology, metal organic frameworks | ABSTRACT In this study, a 3D crystalline metal organic framework based on catecholate linkers was successfully synthesized. The resulting material was obtained by combining titanium isopropoxide (TTIP) and H6THO (where THO6- = triphenylene-2,3,6,7,10,11-hexakis(olate)), known as Ti-76. Its crystallinity was analyzed based on powder X-ray diffraction (PXRD) in combining with the charge-flipping method, by using the program “superflip”. The result showed that the obtaining material is highly crystalline with 3D framework as expected. More specifically, solution was obtained in P21 3 space group with cell parameter a = 17.996 Å. The topology was also determined srs net with double interpenetration. TÓM TẮT Trong nghiên cứu này vật liệu khung cơ kim cấu trúc tuần hoàn không gian 3 chiều đã được tổng hợp thành công dựa trên dẫn xuất của phenol. Vật liệu được tạo thành do sự kết hợp giữa titanium isopropoxide (TTIP) và hợp chất H6THO (trong đó THO6- = triphenylene-2,3,6,7,10,11-hexakis(olate)), được gọi là Ti-76. Độ kết tinh của vật liệu được phân tích dựa trên nhiễu xạ tia X dạng bột (PXRD). Cấu trúc của vật liệu được phân tích dựa trên giản đồ PXRD kết hợp với phương pháp “charge filipping”, sử dụng phần mềm “superflip”. Kết quả cho thấy vật liệu có độ kết tinh cao, có cấu trúc tuần hoàn không gian ba chiều như mong đợi. Cụ thể, vật liệu kết tinh với kiểu mạng tinh thể lập phương với nhóm đối xứng P213 và kích thước ô mạng cơ sở, a = 17,996 Å. “Topology” của vật liệu cũng được xác định, srs với khung sườn đan xen bậc 2. |