The procedures for the production and the orientation of long fibers from Nypa fruiticans petioles were developed in our study. The unidirectional (UD) composites based on Nypa fruitican fibers and polypropylene (PP) were produced. The processing conditions such as fiber volume fraction, processing temperature were investigated respectively. In order to enhance the interfacial stability of the obtained composites, chemical treatment on fibers and matrix were carried out. Fibers were respectively treated with alkali, acetylation, silane. On the other hand, PP was treated with maleic-anhydride grafted PP (MAPP). The mechanical properties of these treated composites were observed and compared to figure out the optimum condition. In addition, chemical properties of fiber and composites were determined to explain the results.
Trích dẫn: Văn Phạm Đan Thủy, Phạm Văn Toàn, Đặng Huỳnh Giao và Đoàn Văn Hồng Thiện, 2020. Tổng hợp sợi nano carbon/ZnO bằng kỹ thuật quay điện hóa. Tạp chí Khoa học Trường Đại học Cần Thơ. 56(3A): 1-8.
Văn Phạm Đan Thủy, Đoàn Thị Ngọc Dung, Trương Hà Phương Ân, Nguyễn Thanh Việt, 2014. ẢNH HƯỞNG CỦA THỜI GIAN PHẢN ỨNG VÀ NỒNG ĐỘ DUNG DỊCH KIỀM TRONG QUÁ TRÌNH TÁI CHẾ NHỰA PET BẰNG PHƯƠNG PHÁP HÓA HỌC. Tạp chí Khoa học Trường Đại học Cần Thơ. 35: 40-45
Văn Phạm Đan Thủy, Trương Hà Phương Ân, Nguyễn Thanh Việt, 2015. Tái chế nhựa polyethylene terephthalate (PET) và ứng dụng nhựa đã qua tái chế. Tạp chí Khoa học Trường Đại học Cần Thơ. 39: 57-65
Tạp chí khoa học Trường Đại học Cần Thơ
Lầu 4, Nhà Điều Hành, Khu II, đường 3/2, P. Xuân Khánh, Q. Ninh Kiều, TP. Cần Thơ
Điện thoại: (0292) 3 872 157; Email: tapchidhct@ctu.edu.vn
Chương trình chạy tốt nhất trên trình duyệt IE 9+ & FF 16+, độ phân giải màn hình 1024x768 trở lên