Title:

Synthesis gold nanostructure using extracts of lemon

Từ khóa:

Chanh, cấu trúc nano, hoá học xanh, vàng

Keywords:

Green chemistry, gold, lemon, nanostructure

ABSTRACT

Gold nanoparticles were synthesised by a redox method using gold chloride, extract of lemon, and polyvinylpyrrolidone as a stabilizer. The optimal conditions for synthesis of gold nanoparticle was obtained, including the ratio of lemon juice to Au⁺ of 1:1,  reaction time of 45 minutes, and reaction temperature of 65^oC. UV-Vis spectrophotometer was used to detect the concentration of Au ions. The maximum of adsorption peaks were obtained in a range of 538 to 570 nm. At the optimal conditions, gold nanoparticles were analyzed using Transmission Electron Microscopy (TEM) to observe the surface characteristics. The average diameter of gold nanoparticles was 13,6 ± 5,48 nm that was determined by the TEM image and an imageJ software.

TóM TắT

Tổng hợp nano vàng bằng phương pháp oxi hóa khử, chất khử được sử dụng là dịch chiết chanh, chất oxi hóa là muối vàng chlorua (HAuCl₄), chất ổn định là polyvinylpyrrolidone (PVP). Tỉ lệ Au⁺ và dịch chiết chanh 1:1, nhiệt độ phản ứng ở 65^oC, và thời gian phản ứng là 45 phút là điều kiện tối ưu. Quang phổ hấp thụ UV-Vis được sử dụng để xác định sự hiện diện của nano vàng trong dung dịch sau phản ứng. Đỉnh hấp thụ cực đại nằm trong khoảng từ 538 - 570 nm. Mẫu nano vàng được tổng hợp dựa theo những điều kiện tối ưu. Sau đó, mẫu được tiến hành phân tích một số tính chất đặc trưng như: hình dáng nano vàng được xác định thông qua kính hiển vi điện tử truyền qua (TEM), kích thước trung bình hạt là 13,6 ± 5,48 nm được xác định bởi ảnh TEM và phần mềm Image J.