Title:

Synthesis of zeolitic imidazolate framework base on mixed two imidazolate linkers and its affinity to CO₂

Từ khóa:

Vật liệu khung cơ kim cấu trúc zeolite, imidazole, đường hấp phụ đẳng nhiệt

Keywords:

Zeolitic imidazole frameworks, linker imidazole, adsorption isotherm

ABSTRACT

Zeolitic imidazole framework-HL1 (ZIF-HL1) is solvothermally synthesized by the reaction of zinc nitrate hexahydrate and the mixture of two imidazolate linkers, 2-methylimidazole and 5-benzimidazole in N,N-dimethylformamide. The structure of ZIF-HL1 was determined by X-ray diffraction analysis, which is indicative the cubic system with cell parameters of a = b = c = 17.4512 Å and V_cell = 5314.64 ų. This material was also demonstrated to be highly porous, water stable, and exhibited high affinity to CO₂. The CO₂ isosteric heat adsorption of ZIF-HL1 of 29 kJ mol^-1 is competitive to reported ZIFs with highest CO₂ affinity.

TÓM TẮT

Vật liệu khung cơ kim cấu trúc zeolite-HL1 (ZIF-HL1) được tạo thành từ phản ứng nhiệt dung môi của kẽm nitrate với hỗn hợp hai linker imidazole, 2-methylimidazole và 5-benzimidazole, trong dung môi N,N-dimethylformamide. Cấu trúc của ZIF-HL1 được xác định bằng phân tích nhiễu xạ tia X, cho kết quả của hệ tinh thể lập phương với các thông số mạng cơ sở a = b = c = 17.45 Å và V_{ô mạng} = 5314.64 ų. Vật liệu ZIF-HL1 còn thể hiện là một vật liệu có độ xốp cao, bền trong nước và có ái lực tốt với CO₂. Nhiệt hấp phụ CO₂ của ZIF-HL1 là 29 kJ mol^-1, được xếp vào hàng các vật liệu ZIF đã công bố có ái lực tốt nhất với CO₂.

Trích dẫn: Liêu Anh Hào, Nguyễn Ngọc Khánh Anh, Nguyễn Duy Khánh, Nguyễn Thị Diễm Hương và Nguyễn Thị Tuyết Nhung, 2017. Tổng hợp vật liệu khung cơ kim cấu trúc zeolite dựa trên hỗn hợp hai dẫn xuất imidazole và khả năng tương tác của vật liệu với CO₂. Tạp chí Khoa học Trường Đại học Cần Thơ. 50a: 6-11.